該方法基于新穎的離散/堆疊成型概念，使用立體光刻、層壓固體制造、激光選擇性燒結、3D打印、熔融沉積建模等不同方法。獲得長壽命金屬模具或非金屬低壽命模具。該方法具有技術、成本低、設計制造周期短等特點。

This method is based on a novel concept of discrete/stacked forming, using various methods such as stereolithography, laminated solid manufacturing, laser selective sintering, 3D printing, and melt deposition modeling. Obtain long-life metal molds or non-metallic low life molds. This method has the characteristics of advanced technology, low cost, and short design and manufacturing cycle.

使用高速切削加工模具：

Using high-speed cutting molds:

生產中廣泛使用的高速切削機床的速度約為每分鐘15，00025，000轉。使用高速切割可以將加工效率提高10倍以上，縮短成型時間。高速切割和精加工后的模具表面只需稍加拋光即可使用，節省大量研磨拋光時間。

The speed of the high-speed cutting machine widely used in production is about 15000 to 25000 revolutions per minute. The use of high-speed cutting can increase processing efficiency by more than 10 times and shorten molding time. The surface of the mold after high-speed cutting and precision machining only needs to be slightly polished to use, saving a lot of grinding and polishing time.

使用鋁合金材料制作塑料模具：

Using aluminum alloy materials to make plastic molds:

鋁合金材料因其重量輕、切削性能好、導熱系數高等特點，在制造塑料模具中得到越來越多的應用。使用鋁合金材料制作模具可以在縮短成型周期和降低成本方面取得良好的效果。國外有廠家生產塑料模具用鋁合金材料。鋁合金制成的塑料模具使用壽命為100萬次。如果對型腔表面進行化學處理，使用壽命可達000萬200萬次。

Aluminum alloy materials are increasingly being used in the manufacturing of plastic molds due to their lightweight, good cutting performance, and high thermal conductivity. Using aluminum alloy materials to make molds can achieve good results in shortening the molding cycle and reducing costs. There are foreign manufacturers producing aluminum alloy materials for plastic molds. The service life of plastic molds made of aluminum alloy is 1 million times. If the surface of the mold cavity is chemically treated, its service life can reach 10 to 2 million times.

使用鋅基低熔點金制作模具：

Using zinc based low melting point gold to make molds:

使用低熔點合金制作模具具有成本低，成型周期短的優點。特別是，這種成型方法與快速成型技術的結合是有效的。使用低熔點合金的快速成型方法特別適用于大型蓋板模具和大型吹塑和吸塑模具的快速制造。當用于蓋板模具時，可以快速生產樣品。另一方面，當用作正式的硬模制造實驗時，可以避免造成無法彌補的缺陷。由低熔點合金制成的泡罩和吹塑模具的使用壽命為 50，000 件。這種成型方法的另一個優點是材料可以在模具報廢后熔化和重復使用。

The use of low melting point alloys to make molds has the advantages of low cost and short forming cycle. Especially, the combination of this molding method and rapid prototyping technology is effective. The rapid prototyping method using low melting point alloys is particularly suitable for the rapid manufacturing of large cover plate molds and large blow molding and vacuum molding molds. When used for cover plate molds, samples can be produced quickly. On the other hand, when used as a formal hard mold manufacturing experiment, it can avoid causing irreparable defects. The service life of bubble caps and blow molding molds made of low melting point alloys is 50000 pieces. Another advantage of this molding method is that the material can melt and be reused after the mold is scrapped.

其他快速成型成型技術：

Other rapid prototyping technologies:

如環氧樹脂模具、噴涂成型模具、氮氣瓶等。環氧樹脂鑲嵌鋼模具用于汽車面板模具。熱噴涂法用于制造模腔，主要用于生產聚氨酯泡沫，在聚氨酯工業中得到了廣泛的應用。氮氣筒在沖壓模具上的應用可以有效簡化模具結構，提高沖壓工藝性能。

Such as epoxy resin molds, spray molding molds, nitrogen bottles, etc. Epoxy resin embedded steel molds are used for automotive panel molds. Thermal spraying method is used to manufacture mold cavity, which is mainly used to produce polyurethane foam, and has been widely used in polyurethane industry. The application of nitrogen cylinder in stamping molds can effectively simplify the mold structure and improve the stamping process performance.